Use Of Sodium Carboxymethyl Cellulose CMC And Its Taboo
Edit: Hangzhou Hongbo New Materials Co.,Ltd    Date: Jul 10, 2017

1. Sodium Carboxymethyl Cellulose CMC directly mixed with water, prepared into a paste glue, the reserve. When the Sodium Carboxymethyl Cellulose CMC sodium paste is configured, a certain amount of clean water is first added to the mixing tank with the stirring device, and the Sodium Carboxymethyl Cellulose CMC is slowly and evenly distributed in the case of opening the stirring device Ingredients in the tank, keep stirring, so that Sodium Carboxymethyl Cellulose CMC and water fully integrated, Sodium Carboxymethyl Cellulose CMC can be fully dissolved.

In the melting of Sodium Carboxymethyl Cellulose CMC, the reason why the average spread, and constantly stirring, the purpose is to "in order to prevent Sodium Carboxymethyl Cellulose CMC and water meet, the occurrence of agglomeration, agglomeration, reduce the carboxymethyl cellulose Sodium dissolved amount of the title ", and the progress of Sodium Carboxymethyl Cellulose CMC dissolution rate. The time of agitation is not consistent with the time of complete melting of sodium carboxymethylcellulose. It is two concepts. In general, the agitation time is much shorter than the time required for the complete melting of sodium carboxymethylcellulose. The time required depends on the details.

The determination of the agitation time is based on the fact that when Sodium Carboxymethyl Cellulose CMC is dispersed evenly in water and no significant large agglomerates are present, they can be stirred so that sodium carboxymethylcellulose and water are in a standing state Under the mutual osmosis, mutual integration. Determine the time required for the complete dissolution of sodium carboxymethylcellulose in such a way as follows:

(1) Sodium Carboxymethyl Cellulose CMC and water completely bonded, there is no solid-liquid separation between the two;

(2) mixed paste was the same state of uniform, smooth and smooth surface;

(3) mixed paste bright color close to colorless and transparent, no paste in the granular material. From the Sodium Carboxymethyl Cellulose CMC was put into the mixing tank and the water began to mix, to the complete dissolution of Sodium Carboxymethyl Cellulose CMC, the required time between 10 to 20 hours.

2. Sodium Carboxymethyl Cellulose CMC and dried raw materials such as white sugar, mixed in dry form, and then dissolved in water. Manipulation, the first Sodium Carboxymethyl Cellulose CMC and sugar and other raw materials in accordance with a certain percentage of dry, placed in a stainless steel mixer, close the top of the mixer, so that the mixer material in a closed state.

Then, the mixer was turned on, and sodium carboxymethylcellulose and other raw materials were thoroughly mixed. The mixed carboxymethylcellulose sodium mixture is then slowly spread evenly onto the tank filled with water and continuously agitated, followed by manipulation of the first dissolution method described above.

3. When using sodium carboxymethylcellulose in liquid or syrupy food, it is advisable to homogenize the mixed material in order to achieve a more delicate tissue condition and no effect. The pressure and temperature used when homogenizing are determined by the characteristics of the material and the quality requirements of the product.